| Laboratory Data | Typical Properties |
| Flash, PMCC*, Minimum | 106 F |
| Density, Weight/Gallon @ 77 F (25 C) | 7.4 0.1lbs./gallon |
| Specific Gravity @ 60 °F (15.6 °C) | 0.89 |
| Recommended Dry Film Thickness over Metal Profile | 1.3 mils |
| Theoretical Coverage @ Recommended DFT | 592 sq.ft/gallon |
| Non-Volatile % by Weight | 55 ± 2 |
| Non-Volatile & by Volume | 48 ± 2 |
| Volatile Organic Content (VOC), Maximum | 3.48lbs./gallon |
| Approximate Dry to Touch Time @ 77 °F (25 °C) | 1 hour |
| Cure Time | 24 hours |
| High Temperature Flow Point, Minimum | 300 °F |
Surface Preparation
The maximum performance of TECTYL® 506 can be achieved only when the metal surfaces to be protected are clean, dry and free of rust, oil and mill scale. Daubert Chemical Company recommends that the metal substrate temperature be 50 - 95°F (10 - 35 °C) at the time of product application.
Application
TECTYL® 506 is formulated to be used as supplied. Ensure uniform consistency prior to use. Continued stirring is generally not required. If the product thickens due to cold storage or loss of solvent during use, contact Daubert Chemical Company. DO NOT THIN TECTYL® 506. Incorrect thinning will affect film build, dry time and product performance. Daubert Chemical Company recommends that the ambient and product temperature be 50 - 95°F (10 - 35 °C) at time of application. TECTYL® 506. can be spray of dip applied. DO NOT FREEZE TECTYL® 506.
Removal
TECTYL® 506 can be removed with TECTYL® HPS solventborne thinner, vapor degreasing, hot alkaline wash, or low pressure steam. TECTYL® 506 can be removed from fabrics by normal dry cleaning procedures. Avoid the use of chlorinated or highly aromatic solvents when removing from painted surfaces, as these solvents may adversely affect paint.
Storage
Store TECTYL® 506 at temperatures between 50 - 95°F (10 - 35 °C). Mild agitation is recommended prior to use.
Caution
Adequate ventilation is required for cure and to ensure against formation of a combustible liquid. THE PARTIALLY CURED FILM SHOULD NOT BE EXPOSED TO IGNITION SOURCES SUCH AS FLARES, FLAMES, SPARKS EXCESSIVE HEAT, OR TORCHES. Refer to Daubert's Material Safety Data Sheet for additional handling and first aid handling.
Note: The addition of any product over or under this coating is not recommended. The use of additional coatings could result in chemical incompatibility, thus adversely affecting the performance f the coating as stated in the lab data section. If a product other than Daubert Chemical Company's recommended product is required, written authorization must be obtained from Dauber Chemical Company.